RT Journal Article
T1 Effects of aluminum incorporation on the schwertmannite structure and surface properties
A1 Carrero Romero, Sergio
A1 Fernández Martínez, Alejandro
A1 Pérez López, Rafael
A1 Cama, J.
A1 Dejoie, Catherine
A1 Nieto Liñán, José Miguel
AB Schwertmannite is a common nanomineral in acid sulfate environments such as Acid Mine Drainage (AMD) and Acid Sulfate Soils (ASS). Its high surface area and positively charged surface result in a strong affinity towards toxic oxyanions such as arsenate in solution. However, natural precipitation of schwertmannite also involves the accumulation of other impurities, in particular aluminum, an element that is often incorporated into the structure of Fe-oxide minerals, such as goethite and ferrihydrite, affecting their structural and surface properties. However, little is known about the effect of Al incorporation in schwertmannite on the removal capacity of toxic oxyanions found in AMD and ASS (e.g. arsenate). In this paper, schwertmannite samples with variable Al concentration were synthetized and employed in arsenate adsorption isotherm experiments at a constant pH of 3.5. Solid samples before and after arsenate adsorption were characterized using high energy X-ray diffraction and pair distribution function analyses in order to identify structural differences correlated with the Al content as well as variations in the coordination of arsenate adsorbed on the mineral surface. These analyses showed limited Al accumulation on schwertmannite (up to 5%) with a low effect on its structure. The maximum arsenate sorption capacity (258 mmolH2AsO4 molFe-1) was in the range of that with pure schwertmannite, but a higher proportion of inner-sphere coordination was observed. Finally, Al was found to desorb from schwertmannite, with adsorbed arsenate preventing this effect and increasing the stability of the mineral. These results are useful to interpret observations from the field, in particular from river water affected by AMD and ASS, where similar conditions are observed, and where aluminum incorporation is expected.
PB Royal Society of Chemistry
SN 2050-7887
SN 2050-7895 (electrónico)
YR 2022
FD 2022-06-15
LK https://hdl.handle.net/10272/21991
UL https://hdl.handle.net/10272/21991
LA eng
NO Carrero, S., Fernández-Martínez, A., Pérez-López, R., Cama, J., Dejoie, C., & Nieto, J. M. (2022). Effects of aluminum incorporation on the schwertmannite structure and surface properties. In Environmental Science: Processes & Impacts (Vol. 24, Issue 9, pp. 1383-1391). Royal Society of Chemistry (RSC). https://doi.org/10.1039/d2em00029f
NO This paper is part of the PID2020-119196RB-C2 TRAMPA project funded by MCIN/AEI/10.13039/501100011033 and by the “European Union Next Generation EU/PRTR”. S. Carrero was supported by IDAEA-CSIC as a Severo Ochoa Centre of Research Excellence (Spanish Ministry of Science and Innovation, Project CEX2018-000794-S). ESRF data were acquired during the experiment EV-198 at ID22. Funding from the Labex OSUG@2020 (Investissements d'avenir-ANR10 LABX56), supporting the use of TGA-DSC analysis at ISTerre, is acknowledged. Chemical analyses were performed at the laboratories of IDAEA (CSIC) in Barcelona.
DS Repositorio Institucional de la Universidad de Huelva
RD 30 may 2026